System for the electrolytic production of sodium chlorate

System for the electrolytic production of sodium chlorate description/claims

This application is a continuation of PCT/EP2006/069079, filed Nov. 29, 2006, that claims the benefit of the priority date of Italian Patent Application No. MI2005A002298, filed on Nov. 30, 2005, the contents of which are herein incorporated by reference in their entirety.

The invention relates to a process for the industrial electrolytic production of sodium chlorate having a high yield and high electrical efficiency.

The production of chlorates ranks among the most important processes of industrial electrochemistry, since sodium chlorate is the raw matter for the production of sodium perchlorate and chlorite and more importantly of chlorine dioxide, employed for water treatment and for bleaching in the paper industry, as a replacement for chlorine. Sodium chlorate is commonly produced in electrolytic cells of the undivided type starting from a sodium chloride brine at controlled pH, with anodic production of hypochlorite and hypochlorous acid, which quickly disproportionate at the process temperatures (60-90° C.) generating chlorate, while hydrogen evolution takes place at the cathode side.

The electrolytic cells for chlorate production can be of the monopolar or of the bipolar type. In the most common case, they consist of a multiplicity of cathodes and a multiplicity of anodes disposed in a comb-like structure and mutually intercalated.

As regards the construction materials, the anodes generally consist of a titanium substrate activated with suitable catalytic coatings for chlorine evolution, comprising noble metals such as platinum, ruthenium, palladium, iridium, or oxides thereof, as such or in admixture with other stabilising oxides. The cathodes are generally made of a ferrous material, such as, for example, low carbon steels, and are normally not activated. Some catalytic coatings for hydrogen evolution suitable for ferrous cathodic substrates are in fact known in the art, for instance comprising molybdenum and/or tungsten alloys with iron, cobalt or nickel, in the attempt of improving the process voltage and thus decreasing the rather high energy costs; the voltage gain obtained with these types of activation is nevertheless considered too small for justifying the adoption thereof in industrial manufacturing processes.

As regards the details of the chlorate manufacturing process, the electrolyte initially consisting of a sodium chloride brine is either progressively enriched in chlorate until reaching the required concentration in a batch cycle, or it is at least partially withdrawn at the cell outlet and subjected to a chlorate separation process, while a restoration of sodium chloride concentration is simultaneously carried out in the cell. In both cases, the control of pH is an essential factor to keep the efficiency high, due to the competition between the chlorate generation reaction and the anodic oxygen evolution, and even more between the cathodic hydrogen evolution and the undesirable hypochlorite reduction; the optimum pH interval to maximise the efficiency ranges between 6 and 7, and even more preferably between 6.3 and 6.6. To keep these optimum pH values, it is necessary to buffer the process electrolyte, as will be evident to those skilled in the art; for this purpose, the currently existing plants of chlorate electrolytic industrial production resort to the addition of sensible quantities of dichromate ion (3 to 5 g/l), implying a series of annoying secondary problems. The presence of dichromate (and of chromate in equilibrium therewith) is for instance undesirable in the subsequent chlorine dioxide manufacturing process, and its separation from chlorate by crystallisation is hindered by the very similar solubility. Furthermore, the toxicity of hexavalent chromium increases the treatment cost of process exhausts.

It would be desirable to provide a system for sodium chlorate production with low energy consumption making use of a nil or extremely limited amount of chromium compounds.

The invention comprises a system for sodium chlorate production having electrolytic cells fed with a buffered sodium chloride brine, wherein the buffering agent comprises phosphate ions at a concentration not lower than 1 g/l. Phosphate ion concentration, as defined herein, refers to the sum of the concentrations of all the ionic species derived from phosphoric acid according to their mutual equilibrium in aqueous solutions, for instance comprising H2PO4−, HPO42−, PO43− anions and, optionally, the oligomers derived therefrom. In one embodiment, the sodium chloride brine of the system contains chromate and/or dichromate ions at a concentration not higher than 0.1 g/l. In a further embodiment, the sodium chloride brine is free of chromium in any form.

The electrolytic cells of the system of the invention are equipped with cathodes consisting of a ferrous matrix, for instance carbon steel, activated with a coating consisting of a molybdenum or tungsten alloy with a metal comprising iron, cobalt or nickel. The inventors have in fact surprisingly noticed that the voltage decrease observed with this type of alloys, which is limited to 100-150 mV with the brines of the prior art at the usual current densities of industrial processes (2.5-3 kA/m2) reaches 450-500 mV with the sodium chloride brine added with phosphate ions in accordance with the invention. The gain in terms of energy efficiency is therefore so high that it largely justifies resorting to cathodes activated with this type of coating, notwithstanding the higher manufacturing costs. The inventors noticed the surprising efficiency of Fe—Mo alloy coatings in a weight ratio comprised between 30:70 and 70:30, but this kind of effect can be observed also with other formulations. Without wishing the invention to be bound to any particular theory, it might be assumed that the effect of ionic species added to the brine is not only buffering the pH, but also adsorbing to the cathode surfaces, creating films which inhibit the decomposition of the generated chlorate or the undesirable cathodic reduction of hypochlorite. The catalytic effect of coatings such as Fe—Mo alloy can be attributable in part to the higher ionic adsorption and to the formation of inhibiting films of higher efficacy, most likely due to their reduced thickness. Such an effect is already sensible with the chromium oxide polymer films generated under the effect of chromate or dichromate adsorption, but it is much more evident in presence of films containing phosphoric species. The cathodic catalytic coating as herein described can be applied galvanically, with a thickness comprised between 10 and 50 micrometres.

A series of cathodes for an electrolytic cell was prepared starting from 0.5 mm thick carbon steel perforated sheets. The sheets were degreased in a saturated solution of caustic soda in ethanol for 5 minutes and then etched in 25% by weight HCl for 2 minutes. The samples were then rinsed with distilled water, dried, weighed and immersed in a bath for Fe—Mo alloy electrodeposition. The bath was prepared by dissolution of 9 g/l FeCl3, 40 g/l Na2MoO4, 75 g/l NaHCO3 and 45 g/l Na2P2O7 in distilled water, and the deposition was carried out at a constant current density of 100 mA/cm2 at a temperature of 60° C., making use of a platinum fine mesh as the counterelectrode, under stirring. The deposition was protracted until obtaining a 20 micrometre thick alloy comprised of 47% by weight molybdenum and 53% by weight iron, as detected by a subsequent EDS test (X-ray energy dispersion spectroscopy).

The so obtained samples were installed in a commercial cell for chlorate production, intercalated in a comb-like fashion with a series of titanium anodes activated with ruthenium and titanium oxides as known in the art, and subjected to a series of electrochemical characterisations as disclosed hereafter. Another cell equivalent to the former was also assembled, the only difference being the cathodes, obtained from the same carbon steel perforated sheet but free of catalytic coating.

The cells of example 1, one comprising Fe—Mo alloy-coated steel cathodes and the other with non-activated cathodes, were employed in a discontinuous sodium chlorate manufacturing process. The feed brine had an initial composition of 300 g/l NaCl added with 3 g/l of Na2Cr2O7, as known in the art. The initial feed pH was 6.41. Each of the two cells was operated at a current density of 2.5 kA/m2 at a temperature of 61° C., and the test was protracted for 8 hours, until obtaining a chlorate concentration of about 0.8 mol/l. The cell with the activated cathodes worked at a very stable voltage, comprised between 3.01 and 3.02 V, with a 98% efficiency. The cell with the non activated cathodes worked at a voltage comprised between 3.14 and 3.17 V with 97% efficiency. In both cases, the hypochlorite concentration was quickly stabilised at a value of 0.06 mol/l.

• Provisional Patent
• Utility Patent

• What Is a Patent?
• What Is a Trademark or Servicemark?
• What Is a Copyright?
• Patent Laws