Semiconductor image device package with die receiving through-hole and method of the same

Semiconductor image device package with die receiving through-hole and method of the same description/claims

This application is a Divisional of co-pending application Ser. No. 11/647,217, filed on Dec. 29, 2006, and for which priority is claimed under 35 U.S.C. § 120, the entire contents of which are hereby incorporated by reference.

1. Field of the Invention

This invention relates to a structure of wafer level package (WLP), and more particularly to a fan-out wafer level package with die receiving through-hole and inter-connecting through holes formed within the substrate to improve the reliability and to reduce the device size.

2. Brief Description of the Prior Art

In the field of semiconductor devices, the device density is increased and the device dimension is reduced, continuously. The demand for the packaging or interconnecting techniques in such high density devices is also increased to fit the situation mentioned above. Conventionally, in the flip-chip attachment method, an array of solder bumps is formed on the surface of the die. The formation of the solder bumps may be carried out by using a solder composite material through a solder mask for producing a desired pattern of solder bumps. The function of chip package includes power distribution, signal distribution, heat dissipation, protection and support . . . and so on. As a semiconductor become more complicated, the traditional package technique, for example lead frame package, flex package, rigid package technique, can't meet the demand of producing smaller chip with high density elements on the chip.

Furthermore, because conventional package technologies have to divide a dice on a wafer into respective dies and then package the die respectively, therefore, these techniques are time consuming for manufacturing process. Since the chip package technique is highly influenced by the development of integrated circuits, therefore, as the size of electronics has become demanding, so does the package technique. For the reasons mentioned above, the trend of package technique is toward ball grid array (BGA), flip chip (FC-BGA), chip scale package (CSP), Wafer level package (WLP) today. “Wafer level package” is to be understood as meaning that the entire packaging and all the interconnections on the wafer as well as other processing steps are carried out before the singulation (dicing) into chips (dies). Generally, after completion of all assembling processes or packaging processes, individual semiconductor packages are separated from a wafer having a plurality of semiconductor dies. The wafer level package has extremely small dimensions combined with extremely good electrical properties.

WLP technique is an advanced packaging technology, by which the die are manufactured and tested on the wafer, and then the wafer is singulated by dicing for assembly in a surface-mount line. Because the wafer level package technique utilizes the whole wafer as one object, not utilizing a single chip or die, therefore, before performing a scribing process, packaging and testing has been accomplished; furthermore, WLP is such an advanced technique so that the process of wire bonding, die mount and under-fill can be omitted. By utilizing WLP technique, the cost and manufacturing time can be reduced, and the resulting structure of WLP can be equal to the die; therefore, this technique can meet the demands of miniaturization of electronic devices.

Though the advantages of WLP technique mentioned above, some issues still exist influencing the acceptance of WLP technique. For instance, the CTE difference (mismatching) between the materials of a structure of WLP and the mother board (PCB) becomes another critical factor to mechanical instability of the structure. A package scheme disclosed by U.S. Pat. No. 6,271,469 suffers the CTE mismatching issue. It is because the prior art uses silicon die encapsulated by molding compound. As known, the CTE of silicon material is 2.3, but the CTE of molding compound is around 40-80. The arrangement causes chip location be shifted during process due to the curing temperature of compound and dielectric layers materials are higher and the inter-connecting pads will be shifted that will causes yield and performance problem. It is difficult to return the original location during temperature cycling (it caused by the epoxy resin property if the curing Temp near/over the Tg). It means that the prior structure package can not be processed by large size, and it causes higher manufacturing cost.

Further, some technical involves the usage of die that directly formed on the upper surface of the substrate. As known, the pads of the semiconductor die will be redistributed through redistribution processes involving a redistribution layer (RDL) into a plurality of metal pads in an area array type. The build up layer will increase the size of the package. Therefore, the thickness of the package is increased. This may conflict with the demand of reducing the size of a chip.

Further, the prior art suffers complicated process to form the “Panel” type package. It needs the mold tool for encapsulation and the injection of mold material. It is unlikely to control the surface of die and compound at same level due to warp after heat curing the compound, the CMP process may be needed to polish the uneven surface. The cost is therefore increased.

Therefore, the present invention provides a fan-out wafer level packaging (FO-WLP) structure with good CTE performance and shrinkage size to overcome the aforementioned problem and also provide the better board level reliability test of temperature cycling.

The object of the present invention is to provide a fan-out WLP with excellent CTE performance and shrinkage size.

The further object of the present invention is to provide a fan-out WLP with a substrate having die receiving through-hole for improving the reliability and shrinking the device size.

The present invention discloses a structure of package comprising: a substrate with a die receiving through hole, a connecting through hole structure and a first contact pad; a die having micro lens area disposed within the die receiving through hole; a transparent cover covers the micro lens area; a surrounding material formed under the die and filled in the gap between the die and sidewall of the die receiving though hole; a dielectric layer formed on the die and the substrate; a re-distribution layer (RDL) formed on the dielectric layer and coupled to the first contact pad; a protection layer formed over the RDL; and a second contact pad formed at the lower surface of the substrate and under the connecting through hole structure.

The material of the substrate includes epoxy type FR5, FR4, BT, silicon, PCB (print circuit board) material, glass or ceramic. Alternatively, the material of the substrate includes alloy or metal; it prefers that the CTE (Coefficient of Thermal Expansion) of the substrate is close to the CTE of mother board (PCB) having CTE around 16 to 20. The material of the dielectric layer includes an elastic dielectric layer, a photosensitive layer, a silicone dielectric based layer, a siloxane polymer (SINR) layer, a polyimides (PI) layer or silicone resin layer.

Further scope of the applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.