| Methanol-tolerant cathode catalyst composite for direct methanol fuel cells -> Monitor Keywords |
|
|
 
Methanol-tolerant cathode catalyst composite for direct methanol fuel cellsRelated Patent Categories: Chemistry: Electrical Current Producing Apparatus, Product, And Process, Fuel Cell, Subcombination Thereof Or Methods Of Operating, Catalytic Electrode Structure Or CompositionMethanol-tolerant cathode catalyst composite for direct methanol fuel cells description/claimsThe Patent Description & Claims data below is from USPTO Patent Application 20060063061, Methanol-tolerant cathode catalyst composite for direct methanol fuel cells. Brief Patent Description - Full Patent Description - Patent Application Claims
RELATED APPLICATION [0001] This application claims the benefit of U.S. patent application Ser. No. 10/260,780, filed Sep. 27, 2002. FIELD OF THE INVENTION [0003] The present invention relates generally to direct methanol fuel cells, and, more particularly, to cathode catalyst compositions for direct methanol fuel cells. BACKGROUND OF THE INVENTION [0004] Fuel cells are considered a possible alternative to direct combustion engines to power transportation vehicles and to possibly furnish electrical energy to a power distribution grid for home and business use. In a fuel cell, fuels are chemically reacted with an oxidant whereby a direct current is produced at a low voltage across individual cells and stacks of cells produce useful power. Catalyst materials promote the chemical reactions of the fuels (typically hydrogen or methanol) and oxidant (typically pure oxygen or air). [0005] In a generic embodiment shown in FIG. 1, a fuel cell 10 includes an anode electrode 14 for the fuel oxidation, a cathode electrode 16 for the oxidant reduction, and a solid-state polymer electrolyte membrane 18 therebetween to provide an ionic conduction path. The combination of anode electrode 14, cathode electrode 16, and membrane 18 is conventionally called a membrane electrode assembly (MEA) 12. A suitable catalyst is disposed adjacent the interfaces of electrode/membrane surfaces 14/18 and 16/18 so that the fuel is oxidized at the anode/membrane interface 14/18 to produce ions that traverse the membrane to complete the oxidant reduction at the cathode/membrane interface 16/18. Fuel 24 is distributed over anode 14 of MEA 12 by fuel distribution plate 22 and unreacted fuel and reaction products 26 are exhausted. Oxidant 32 is distributed over cathode 16 of MEA 12 by oxidant distribution plate 28 and excess oxidant and reaction products 34 are exhausted. As a result, electrons generated at anode 14 travel through an external circuit (not shown) back to cathode 16. The electrons constitute the flow of electrical current that provides energy to components connected to the external circuit. [0006] The most common fuel used in the development of polymer electrolyte membrane fuel cells has been hydrogen, either in a pure form or furnished as a reformate from hydrocarbon products. Yet another approach is to directly use a liquid methanol solution in direct methanol fuel cells (DMFCs) to avoid the complications associated with supplying pure hydrogen or providing a separate system for reforming hydrocarbons to provide reformed hydrogen. DMFCs with a solid polymer electrolyte can provide high current density at low temperature and have a relatively simple fuel cell construction. Methanol is a renewable fuel material and can be readily transported and supplied with existing transportation and distribution infrastructure for liquid fuels. Both hydrogen fuel cells and DMFCs have the generic structure shown in FIG. 1. [0007] In a DMFC, catalysts promote electrode reactions at the cathode and the anode, where a metric of performance is the catalytic activity per unit mass of catalytic metal. This metric is directly related to the efficiency and output power of the cells and to the manufactured cost of the cells. Platinum black was an early cathode catalyst in an ion-exchange MEA for hydrogen fuel cells, typically a gas diffusion electrode substrate with one surface coated with platinum black in an amount of 4 to 10 mg cm.sup.-2 of the MEA. [0008] To improve the utilization efficiency of platinum, a catalyst was developed with a platinum alloy supported on conductive carbon or an unsupported platinum alloy, which was mixed with an ion-exchange polymer, coated on an electrode substrate, and joined to an ion-exchange membrane by painting, hot pressing, or the like, to form the MEA. This process permitted the thickness and composition of the catalyst layer to be controlled so that the catalyst was more effectively utilized in the electrode reaction. A loading of platinum or platinum alloy of only 0.1 to 1.0 mg cm.sup.-2 was needed to produce a performance equivalent to prior art hydrogen fuel cells. [0009] This reduced loading that has been demonstrated for hydrogen fuel cells has not been achieved for DMFCs. In a DMFC, some methanol crosses through the membrane from the anode and reacts at the cathode, competing with the oxygen reduction reaction for active catalyst surface sites. Reducing the catalyst loading results in fewer active sites available for the oxygen reduction reaction, as well as limiting the ability of the catalyst to handle methanol crossover, with a concomitant reduction in the potential of the DMFC cathode. Thus, methanol crossover to the cathode not only lowers fuel utilization, but also adversely affects the oxygen cathode with overall lower cell performance. [0010] One way to reduce the effect of methanol crossover on DMFC performance is to simply reduce methanol crossover by developing a membrane that is less permeable to methanol. However, this has not yet been fully realized in the art. Other ways to reduce methanol crossover include lower methanol feed concentration and optimized cell design. [0011] The present invention recognizes that performance losses associated with methanol crossover arise from the fact that most Pt-based cathode systems are catalytically active to methanol oxidation under normal cell operating conditions with a resulting net cathode potential from oxygen reduction reaction potential reduced by the methanol oxidation reaction. In accordance with the present invention, a Pt-alloy catalyst has been identified that is less catalytically active for methanol oxidation, while having equal or increased catalytic activity for oxygen reduction. [0012] Various objects, advantages and novel features of the invention will be set forth in part in the description which follows, and in part will become apparent to those skilled in the art upon examination of the following or may be learned by practice of the invention. The objects and advantages of the invention may be realized and attained by means of the instrumentalities and combinations particularly pointed out in the appended claims. SUMMARY OF THE INVENTION [0013] The present invention is a direct methanol fuel cell (DMFC) having a methanol fuel supply, oxidant supply, and a membrane electrode assembly (MEA) formed of an anode electrode and a cathode electrode with a solid polymer electrolyte membrane therebetween, a methanol oxidation catalyst adjacent the anode electrode and the membrane, an oxidant reduction catalyst adjacent the cathode electrode and the membrane, wherein the improvement comprises an oxidant reduction catalyst layer containing platinum-chromium so that oxidation at the cathode of methanol that crosses from the anode through the membrane to the cathode is reduced with a concomitant increase of net electrical potential at the cathode electrode. [0014] In one embodiment, the platinum-chromium catalyst is supplied at a loading less than 1 mg cm.sup.-2 and the cathode catalyst layer includes a perfluorinated ion exchange polymer in a volume percent between 35% and 55%. BRIEF DESCRIPTION OF THE DRAWINGS [0015] The accompanying drawings, which are incorporated in and form a part of the specification, illustrate embodiments of the present invention and, together with the description, serve to explain the principles of the invention. In the drawings: [0016] FIG. 1 pictorially depicts the component parts of a fuel cell having functions described herein. [0017] FIG. 2 graphically depicts CO stripping voltammograms for platinum-chromium/C and Pt/C catalysts to illustrate the low catalytic activity of platinum-chromium/C for methanol oxidation relative to Pt/C. [0018] FIG. 3 graphically depicts polarization plots representing electro-oxidation of crossover methanol at platinum-chromium/C and Pt/C electrodes to further demonstrate the relatively low catalytic activity of platinum-chromium/C for methanol oxidation. [0019] FIG. 4 graphically compares the performance of two DMFCs, one with a platinum-chromium/C cathode and the other with a Pt/C cathode. [0020] FIG. 5 graphically compares the performance of three (3) DMFCs with MEAs using platinum-chromium/C with one MEA using Pt/C to illustrate performance improvement consistency. Continue reading about Methanol-tolerant cathode catalyst composite for direct methanol fuel cells... Full patent description for Methanol-tolerant cathode catalyst composite for direct methanol fuel cells Brief Patent Description - Full Patent Description - Patent Application Claims Click on the above for other options relating to this Methanol-tolerant cathode catalyst composite for direct methanol fuel cells patent application. ###  How KEYWORD MONITOR works... a FREE service from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like Methanol-tolerant cathode catalyst composite for direct methanol fuel cells or other areas of interest. ### Previous Patent Application: Catalyst and a method for manufacturing the same Next Patent Application: Lithium secondary battery Industry Class: Chemistry: electrical current producing apparatus, product, and process ### FreshPatents.com Support Thank you for viewing the Methanol-tolerant cathode catalyst composite for direct methanol fuel cells patent info. IP-related news and info Results in 0.46925 seconds Other interesting Feshpatents.com categories: Novartis , Pfizer , Philips , Polaroid , Procter & Gamble , 174 |
 * Protect your Inventions * US Patent Office filing 
PATENT INFO |
|