| High tensile modulus nonwoven fabric for cleaning printer machines -> Monitor Keywords |
|
|
  High tensile modulus nonwoven fabric for cleaning printer machinesUSPTO Application #: 20080085649Title: High tensile modulus nonwoven fabric for cleaning printer machines Abstract: A nonwoven fabric having high tensile modulus suitable for cleaning printer cylinders is formed by hydroentangling a fibrous nonwoven web formed from higher-melting polyester fibers, lower-melting binder fibers and woodpulp fibers and then thermally bonding the fabric. (end of abstract) Agent: E I Du Pont De Nemours And Company Legal Patent Records Center - Wilmington, DE, US Inventors: Jaime Marco Vara Salamero, Thomas Edward Benim, Jose-Maria Rodriguez USPTO Applicaton #: 20080085649 - Class: 442327 (USPTO) The Patent Description & Claims data below is from USPTO Patent Application 20080085649. Brief Patent Description - Full Patent Description - Patent Application Claims
BACKGROUND OF THE INVENTION [0001]1. Field of the Invention [0002]The present invention relates to nonwoven fabrics for cleaning cylinders of machinery, such as printing machine cylinders. [0003]2. Description of the Related Art [0004]It is known in the art to use nonwoven fabrics to clean the cylinders of printing machines. U.S. Pat. No. 5,974,976 to Gasparrini et al. describes nonwoven cleaning fabrics having reduced air content and the use of such fabrics to clean the cylinders of a printing press. U.S. Patent Application Publication No. 2002/0187307 to Tanaka et al. describes wet-laid sheets for cleaning printer cylinders. The wet-laid sheets contain between about 5 and 50 weight percent binder fibers and are hydroentangled and creped, followed by heating to fuse the binder fibers after creping. Examples of wet-laid sheets include sheets containing at least 50 percent pulp. [0005]In an effort to reduce costs and to reduce the impact printed materials have on the environment; recycled paper is used as a raw material for printing. However, recycled paper produces more lint than new (i.e., non-recycled) paper. The increased amount of paper lint fibers mixes with ink, solvent, and water creating a semi-solid residue on the blanket and impression cylinders of printing machines. Additionally, unacceptable deformation, or necking, due to elongation of the cleaning fabric can occur as the cloth advances during a wash program. The cleaning fabric would also need to have high paper lint pick up and retention, no surface streaking on the cylinders and high solvent desorption for increasing the cleaning rate. [0006]It would be desirable to provide an improved cleaning fabric for cleaning machine cylinders that has high tensile modulus to avoid fabric elongation while having high paper lint pick up and retention, no surface streaking on the cylinders and high solvent desorption for increasing the cleaning rate at a reasonable cost. BRIEF SUMMARY OF THE INVENTION [0007]In one embodiment this invention is directed to a high strength nonwoven fabric for cleaning cylinders comprising a spunlaced nonwoven fabric comprising between about 5 and 40 weight percent of binder fibers comprising a lower-melting component, between about 25 and 65 weight percent of higher-melting polyester fibers wherein the lower-melting component comprises a polyester copolymer having a lower melting point than the melting point of the higher-melting polyester fibers and between about 35 and 55 weight percent of wood pulp fibers, and wherein the spunlaced fabric is thermally bonded by at least partially softening or melting the sheath component of the binder fibers to provide a thermally bonded spunlaced nonwoven fabric. DETAILED DESCRIPTION OF THE INVENTION [0008]The terms "nonwoven fabric" and "nonwoven web" as used herein refer to a sheet structure of individual fibers that are positioned in a random manner to form a planar material without an identifiable pattern, as opposed to a knitted or woven fabric. [0009]The term "spunlaced nonwoven fabric" as used herein refers to a nonwoven fabric that is produced by entangling fibers in a fibrous nonwoven web using fluid jets. For example, a spunlaced nonwoven fabric can be prepared by supporting a fibrous web on a porous support such as a mesh screen and hydroentangling the web by passing the supported web underneath water jets, such as in a hydraulic needling process. [0010]The term "machine direction" (abbreviated as MD) is used herein to refer to the direction in which a nonwoven web is produced (e.g. the direction of travel of the supporting surface upon which the fibers are laid down during formation of the nonwoven web). The term "cross direction" (abbreviated as XD) refers to the direction generally perpendicular to the machine direction in the plane of the web. [0011]The term "polyester" as used herein is intended to embrace polymers wherein at least 85% of the recurring units are condensation products of dicarboxylic acids and dihydroxy alcohols with linkages created by formation of ester units. This includes aromatic, aliphatic, saturated, and unsaturated di-acids and di-alcohols. A common example of a polyester is poly(ethylene terephthalate) (PET) that is a condensation product of ethylene glycol and terephthalic acid. [0012]The term "binder fiber" is used herein to refer to fibers that are thermally bondable (i.e. meltable or partially meltable) at a temperature below that of the degradation or melting point of higher melting base fibers that are combined with the binder fibers in a nonwoven web. Binder fibers can be homogeneous or can comprise multiple component fibers. The term "multiple component fiber" as used herein refers to a fiber that is composed of at least two distinct polymeric components that have been spun together to form a single fiber. The at least two polymeric components are arranged in distinct substantially constantly positioned zones across the cross-section of the multiple component fibers, the zones extending substantially continuously along the length of the fibers. Multiple component fibers that are suitable for use as binder fibers include a lower melting polymeric component on at least a portion of the peripheral surface thereof. The lower melting polymeric component has a melting point that is lower than the melting point of higher melting base fibers in the web. The term "bicomponent fiber" is used herein to refer to a multiple component fiber that is made from two distinct polymer components. [0013]The term "staple fibers" means natural fibers or cut lengths from filaments. Typically staple fibers have a length of between about 0.25 and 5.0 inches (0.6 and 15.2 cm). [0014]The present invention relates to thermally bonded spunlaced nonwoven fabrics that are suitable for cleaning cylinders in printing machines or other equipment. The nonwoven fabrics that contain binder fibers are useful in decreasing fabric elongation. [0015]Fibrous webs suitable for preparing spunlaced nonwoven fabrics for use in some embodiments of the present invention comprise between about 5 and 40 weight percent binder fibers that comprise a lower-melting polyester copolymer component, between about 5 and 55 weight percent of higher-melting polyester base fibers and between about 40 and 60 weight percent of woodpulp fibers. [0016]The low-melting polyester copolymer component preferably has a melting point that is at least about 100.degree. C. to 140.degree. C. less than the melting point of the higher-melting polyester base fiber component. A binder fiber suitable for use in the present invention is a bicomponent fiber comprising a poly(ethylene terephthalate)copolymer sheath and a poly(ethylene terephthalate)core. An example of a suitable poly(ethylene terephthalate)copolymer comprises an isophthalate copolymer of poly(ethylene terephthalate). [0017]Base fibers suitable for use include poly(ethylene terephthalate) fibers. In one embodiment, the nonwoven fabric can be made from a blend of polyester-based binder fibers and base fibers. It should be understood that the range of polyester used can be adjusted by varying the relative amounts of base fiber and binder fiber. For example, if the amount of base fiber were about 5%, the amount of binder fiber could be present at the higher end of its range. The base fibers can comprise microfibers (fiber denier less than 1 denier) or hydrophilic polyester fibers for their increased absorbency. For example, between about 5 and 10 weight percent of the fibers in the web can comprise microfibers and/or hydrophilic polyester fibers. Examples of hydrophilic polyester fibers include those that are treated with a hydrophilic finish. One example is Hydrofix.RTM. hydrophilic polyester fibers, available from ADVANSA in Germany. Examples of microfibers suitable for use in the present invention include split fibers. Splittable fibers are made by co-spinning two or more distinct polymeric components into multiple component fibers such that the polymeric components form non-interlocking separable segments across the cross-section of the fibers that extend along the length of the fibers. Splittable fiber cross-sections include "chrysanthemum" cross-sections in which alternating polymeric components are petal-shaped and partially overlapped by adjacent segments, side-by-side, segmented pie (wedge-shaped segments), hollow segmented pie, segmented cross, tipped trilobal, and other cross-sections known in the art. Splittable fibers can be incorporated into the fibrous web and split in the hydroentangling step described below. [0018]The nonwoven fabrics of the present invention can be prepared from precursor fibrous webs that are formed using dry-lay techniques, such as one or more carded fibrous layers, one or more air-laid fibrous layers, or a combination thereof. Methods for preparing air-laid webs and carded webs are well known in the art. For example, air-laid webs can be made according to U.S. Pat. No. 3,797,074 to Zafiroglu or by using a Rando Webber manufactured by the Rando Machine Corporation and disclosed in U.S. Pat. Nos. 2,451,915; 2,700,188; 2,703,441; and 2,890,497, the entire contents of which are incorporated herein by reference. Staple fibers having a fiber length between about 30 and 75 mm and fiber denier between about 1 and 15 are generally preferred for preparing carded nonwoven webs. Staple fibers having a fiber length between about 12.7 mm and 25.4 mm and fiber denier between about 0.9 and 4 are generally preferred for preparing air-laid nonwoven webs. The deniers of the binder and base fibers are preferably closely matched for better processability. The base fibers and binder fibers can be admixed in the web during formation in carding, and the like, or by conventional textile blending techniques followed by carding the blended fibers. Alternately, a blend of fibers may be dispersed in an air stream and collected on a foraminous means in an air-laying process. Alternately, individual webs comprising binder fibers and/or base fibers can be layered followed by hydroentangling the combined layers to form a spunlaced nonwoven fabric that has one side richer in the binder fiber than the other side. For example, a web consisting of binder fibers can be layered with a web consisting of base fibers and then hydroentangled. Alternately, one or more of the layers can comprise a blend of binder and base fibers, wherein one of the outer layers has a higher weight percent of binder fibers than the other outer layer. In another embodiment, a sandwiched 3-layer structure can be formed by laying down webs in the configuration binder fiber web/base fiber web/binder fiber web, wherein the binder fiber webs can include binder fibers or a blend of binder and base fibers and the base fiber web can include of base fibers or a blend of binder and base fibers wherein one or both of the binder fiber layers has a higher weight percent of binder fibers than the base fiber layer. The web can then be hydroentanged to form a spunlaced nonwoven fabric that has one or two binder-fiber rich sides. It should be understood that at least one layer of wood pulp fibers is included in the embodiments described above. Fibrous nonwoven webs having a basis weight between about 50 and 120 g/m.sup.2, preferably between about 60 and 110 g/m.sup.2 are suitable for use; however the basis weight can be varied to the extent necessary to develop the desired properties. [0019]Carded webs generally have fibers oriented substantially in the machine direction whereas the fibers in air-laid webs are substantially randomly oriented. Carded webs can be cross-lapped to improve the balance of machine direction and cross direction properties. It is often preferred that the machine and cross direction properties of a nonwoven fabric be balanced, however in one embodiment of the present invention, the nonwoven fabric is prepared from a carded web in which the fibers are substantially oriented in the machine direction. [0020]After forming a fibrous web comprising base fibers and binder fibers, the web is hydroentangled. The hydroentangling (or hydraulic needling) process for producing spunlaced nonwoven fabrics is well known in the art. In the hydroentangling process, the fibrous web is positioned on a screen or other type of apertured support and subjected to a series of high-pressure water jets that cause entangling of the fibers to form a spunlaced nonwoven fabric. Conventional hydraulic needling processes are described in U.S. Pat. No. 3,485,706, to Evans and U.S. Pat. No. 4,891,262 to Nakamae et al., the entire contents of which are incorporated herein by reference. The support member can be porous, such as a metal or plastic belt or screen that is woven from round or other shaped strands, monofilaments or yarns, or a perforated plate. The hydroentangled fabric can be apertured or non-apertured, depending on selection of the support member, as is known in the art. When apertured, the range of aperture size can be from about 13 to 24 mesh. Further, the fabric can be patterned or unpatterned. [0021]After the fibrous web has been hydroentangled, the resulting spunlaced nonwoven fabric is thermally bonded. Thermal bonding conditions are selected such that the lower-melting binder fiber component (e.g. sheath for sheath-core binder fibers) softens or melts but the higher-melting base fiber and the core component of the binder fiber do not melt and retain their fibrous structure. The bonding conditions should be selected such that the final fabric has the desired strength properties. The spunlaced nonwoven fabric can be wound up and thermally bonded at a later time in a separate process. Alternately, thermal bonding can be conducted in-line immediately after hydroentanglement, such as in a heated air dryer. In such a process, excess water can be removed from the spunlaced nonwoven fabric, such as by a vacuum dewatering system or squeeze rolls, prior to passing the fabric through the dryer. In one embodiment, the spunlaced nonwoven fabric is thermally bonded in a through-air dryer in which a heated gas, generally air, is passed through the fabric. The gas is heated to a temperature sufficient to soften or melt the low-melting component of the binder fibers without softening or melting the base fibers to bond the binder and matrix fibers at their crossover points. Through-air bonding generally results in substantially uniform bonding across the width and through the thickness of the fabric, as opposed to surface bonding only. Through-air bonders generally include a perforated drum, which receives the fabric, and a hood surrounding the perforated drum. The heated gas is directed from the hood, through the spunlaced nonwoven fabric, and into the perforated drum. The residence time in the through-air bonder and the temperature of the heated gas is selected to both dry the fabric, if it is wet, and to provide the desired degree of thermal bonding. One or more through-air dryers can be used in series to achieve the desired degree of bonding. It has been found that when the base fibers are poly(ethylene terephthalate) fibers having a melting point of about 250-260.degree. C. and the binder fibers are sheath/core fibers comprising a sheath of low-melting isophthalate copolymer of poly(ethylene terephthalate) having a melting point of about 100-120.degree. C. and a poly(ethylene terephthalate) core, that a bonding air temperature of about 180.degree. C. (fabric temperature of about 130-150.degree. C.) and a residence time between about 8 and 12 seconds in the dryer provides a suitable fabric. The fabric can be thermally bonded in-line immediately after it has been hydroentangled or thermally bonded at later time. Continue reading... Full patent description for High tensile modulus nonwoven fabric for cleaning printer machines Brief Patent Description - Full Patent Description - Patent Application Claims Click on the above for other options relating to this High tensile modulus nonwoven fabric for cleaning printer machines patent application. ###  How KEYWORD MONITOR works... a FREE service from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like High tensile modulus nonwoven fabric for cleaning printer machines or other areas of interest. ### Previous Patent Application: Electric conductive material and method of producing the same Next Patent Application: Infusion fabric allowing high resin infusion rates Industry Class: Fabric (woven, knitted, or nonwoven textile or cloth, etc.) ### FreshPatents.com Support Thank you for viewing the High tensile modulus nonwoven fabric for cleaning printer machines patent info. IP-related news and info Results in 1.8521 seconds Other interesting Feshpatents.com categories: Tyco , Unilever , Warner-lambert , 3m |
||
