| Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied -> Monitor Keywords |
|
|
  Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is appliedUSPTO Application #: 20060205584Title: Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied Abstract: Disclosed are a glass substrate for an information recording medium, having excellent scratch resistance and a light weight and having high fracture toughness, the glass substrate having a fragility index value, measured in water, of 12 μm−1/2 or less or having a fragility index value, measured in an atmosphere having a dew point of −5° C. or lower, of 7 μm−1/2 or less, or the glass substrate comprising, by mol %, 40 to 75% of SiO2, 2 to 45% of B2O3 and/or Al2O3 and 0 to 40% of R′2O in which R′ is at least one member selected from the group consisting of Li, Na and K), wherein the total content of SiO2, B2O3, Al2O3 and R′2O is at least 90 mol %, and a magnetic information recording medium comprising a magnetic recording layer formed on the glass substrate. (end of abstract) Agent: Nixon & Vanderhye, PC - Arlington, VA, US Inventors: Mikio Ikenishi, Atsuko Morita, Xuelu Zou USPTO Applicaton #: 20060205584 - Class: 501066000 (USPTO) Related Patent Categories: Compositions: Ceramic, Ceramic Compositions, Glass Compositions, Compositions Containing Glass Other Than Those Wherein Glass Is A Bonding Agent, Or Glass Batch Forming Compositions, Silica Containing, 40 Percent - 90 Percent By Weight Silica, And Boron, And Aluminum The Patent Description & Claims data below is from USPTO Patent Application 20060205584. Brief Patent Description - Full Patent Description - Patent Application Claims
BACKGROUND OF THE INVENTION [0001] 1. Field of the Invention [0002] The present invention relates to a glass substrate for an information recording medium and a magnetic information recording medium to which the glass substrate is applied. More specifically, the present invention relates to a glass substrate for an information recording medium, which glass substrate is excellent in scratch resistance and light in weight and has high fracture toughness, and a magnetic information recording medium to which the above glass substrate is applied, which medium is typified by a hard disk drive. [0003] 2. Prior Art of the Invention [0004] Conventionally, aluminum, glass, ceramic, or the like is used as a substrate material for a magnetic information recording medium. At present, aluminum and glass are mainly practically used depending upon a size and use. Of these, a glass substrate has no or few surface defects and is excellent in smoothness and surface hardness, so that the extent to which it is used is expanding year after year. As a glass for use as a substrate for a magnetic information recording medium, a chemically strengthened glass according to an ion-exchange method, a glass ceramic, etc., are known. As a chemically strengthened glass, for example, JP-A-1-239036 discloses a chemically strengthened glass substrate for a magnetic disk, which substrate is formed of a glass containing, by weight %, 50 to 65% of SiO.sub.2, 0.5 to 14% of Al.sub.2O.sub.3, 10 to 32% of R.sub.2O (in which R is an alkali metal ion), 1 to 15% of ZnO and 1.1 to 14% of B.sub.2O.sub.3 and having a compressive stress layer formed in the surface thereof by an ion-exchange method. Further, as a crystallized glass, for example, U.S. Pat. No. 5,391,522 discloses a glass ceramic substrate for a magnetic disk, which glass ceramic substrate contains, by weight %, 65 to 83% of SiO.sub.2, 8 to 13% of Li.sub.2O, 0 to 7% of K.sub.2O, 0.5 to 5% of MgO, 0 to 5% of ZnO, 0 to 5% of PbO, provided that MgO+ZnO+PbO=0.5 to 5%, 1 to 4% of P.sub.2O.sub.5, 0 to 7% of Al.sub.2O.sub.3 and 0 to 2% of As.sub.2O.sub.3+Sb.sub.2O.sub.3, the above glass ceramic substrate containing fine Li.sub.2O.2SiO.sub.2 as a main crystal. [0005] In recent years, however, an information recording device such as a magnetic disk drive typified by a hard disk drive is demanded to satisfy a higher recording density and a higher speed of writing and reading data, so that it is required to increase the rotation of a disk. The rotation of a disk is approximately 7,200 rpm at present, and it is expected that the rotation will be 15,000 rpm or larger in the future. In particular, a hard disk drive for a server for processing a large volume of data will be particularly increasingly required to satisfy such a demand. With an increase in the rotation of a recording medium, however, the recording medium is caused to bend and a resonance grows, so that there is increased a risk that the surface of the recording medium collides with a magnetic head to cause a read error or to cause clashing of the magnetic head. In an existing recording medium, therefore, it is difficult to decrease a distance (flying height) between the magnetic head and the recording medium beyond a certain value, so that the above risk is constituting a factor that inhibits an increase in the recording density of a magnetic recording device. The above bending-resonance problem of the recording medium can be overcome by employing a substrate material having a high elastic coefficient. [0006] However, a conventional aluminum substrate has an elastic coefficient of approximately 72 GPa, and a glass substrate has an elastic coefficient of approximately 80 to 100 GPa, so that these substrates cannot comply with an increase in the rotation. There is therefore a trend toward increasing the thickness of a substrate to comply with an increase in the rotation. An increase in the thickness of a substrate involves an increase in weight, so that the power consumption for an increase in the rotation increases. Substrate materials having a smaller weight than an aluminum alloy having a large density (2.76 g/cm.sup.3) are commercially demanded. Further, since an aluminum substrate has a far lower surface hardness than a glass substrate and is therefore liable to undergo plastic deformation, so that the surface of a recording medium may be dented due to a collision between a high-speed revolving substrate and a magnetic head. A glass substrate is excellent over an aluminum substrate in all of elastic coefficient, surface hardness and surface smoothness. However, the glass substrate is more fragile than the aluminum substrate, and a slight scratch formed during its production steps leads to breakage of the glass substrate. For example, when a glass is used for a magnetic disk-substrate, the formation of the magnetic disk requires many working processes such as processing to form a circular form, making of a center hole and processing of surfaces of inner and outer circumferences. During the above processing steps, many scratches that can be start points of fractures occur in a glass edge portion, etc., and slight scratches that are formed not only during the production step but also during handlings such as mounting of the glass to a spindle, etc., may lead to the breakage of the substrate. The above problem gains an importance with an increase in the rotation of a magnetic disk. For overcoming these problems, it comes to be required to provide a substrate glass having a small density and having little or no suceptibility to scratches or a substrate glass having high resistance to progress of glass fracture, that is, high fracture toughness. SUMMARY OF THE INVENTION [0007] Under the circumstances, it is an object of the present invention to provide a glass substrate for an information recording medium, which has a small density and has excellent scratch resistance so that it is little or not at all susceptible to scratches, and further, which has high resistance against progress of fracture, that is, high fracture toughness, as well as a magnetic information recording medium to which the above glass substrate is applied. [0008] For achieving the above object, the present inventors have made diligent studies and as a result have found that a glass substrate having a fragility index value, measured in water and/or a dry atmosphere, of a certain value or smaller or a glass substrate having a specific glass composition can suit the above object as a glass substrate for an information recording medium, and the present invention has been accordingly completed on the basis of the above findings. [0009] That is, the present invention provides: [0010] (1) a glass substrate for an information recording medium, having a fragility index value, measured in water, of 12 .mu.m.sup.-1/2 or less (to be referred to as "glass substrate I for an information recording medium" hereinafter), [0011] (2) a glass substrate for an information recording medium, having a fragility index value., measured in an atmosphere having a dew point of -5.degree. C. or lower, of 7 .mu.m.sup.-1/2 or less (to be referred to as .differential.glass substrate II for an information recording medium" hereinafter), [0012] (3) a glass substrate for an information recording medium, having a fragility index value, measured in water, of 12 .mu.m.sup.-1/2 or less and having a fragility index value, measured in an atmosphere having a dew point of -5.degree. C. or lower, of 7 .mu.m.sup.-1/2 or less (to be referred to as "glass substrate III for an information recording medium" hereinafter), [0013] (4) a glass substrate for an information recording medium as recited in the above (1), (2) or (3), comprising, by mol %, greater than 65%, as a total, of SiO.sub.2 and at least one of B.sub.2O.sub.3 and Al.sub.2O.sub.3, 0 to 20% of RO in which R is at least one member selected from the group consisting of Ma, Ca, Zn, Sr and Ba, 0 to 28% of R'.sub.2O in which R' is at least one member selected from the group consisting of Li, Na and K, 0 to 10% of TiO.sub.2 and 0 to 10% of ZrO.sub.2, the total content of said components being at least 95 mol %, [0014] (5) a glass substrate for an information recording medium, comprising, by mol %, 40 to 75% of SiO.sub.2, 2 to 45% of B.sub.2O.sub.3 and/or Al.sub.2O.sub.3 and 0 to 40% of R'.sub.2O in which R' is at least one member selected from the group consisting of Li, Na and K), wherein the total content of SiO.sub.2, B.sub.2O.sub.3, Al.sub.2O.sub.3 and R'.sub.2O is at least 90 mol % (to be referred to as "glass substrate IV for an information recording medium" hereinafter), [0015] (6) a glass substrate for an information recording medium as recited in the above (5), having a fragility index value, measured in water, of 12 .mu.m.sup.-1/2 or less. [0016] (7) a glass substrate for an information recording medium as recited in the above (5) or (6), having a fragility index value, measured in an atmosphere having a dew point of -5.degree. C. or lower, of 7 .mu.m.sup.-1/2 or less, [0017] (8) a glass substrate for an information recording medium as recited in any one of the above (1) to (7), having a Young's modulus of at least 70 GPa, [0018] (9) a glass substrate for an information recording medium as recited in any one of the above (1) to (8), having a modulus of rigidity of at least 20 GPa, [0019] (10) a glass substrate for an information recording medium as recited in any one of the above (1) to (9), which is made of a glass having a region wherein the glass has a viscosity of at least 1 Pas, in a range of temperatures equivalent to, and higher than, a liquidus temperature of the glass, [0020] (11) a glass substrate for an information recording medium as recited in any one of the above (1) to (10), which is made of a glass having a thermal expansion coefficient of 60.times.10.sup.-7/.degree. C. or greater at a temperature of from 100.degree. C. to 300.degree. C., [0021] (12) a glass substrate for an information recording medium as recited in any one of the above (1) to (11), which has no chemically strengthened layer, [0022] (13) a glass substrate for an information recording medium as recited in any one of the above (1) to (11), which has a chemically strengthened layer, and Continue reading... Full patent description for Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied Brief Patent Description - Full Patent Description - Patent Application Claims Click on the above for other options relating to this Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied patent application. ###  How KEYWORD MONITOR works... a FREE service from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied or other areas of interest. ### Previous Patent Application: Translucent and radio-opaque glass ceramics Next Patent Application: Solarization stable borosilicate glass and uses thereof Industry Class: Compositions: ceramic ### FreshPatents.com Support Thank you for viewing the Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied patent info. IP-related news and info Results in 0.55464 seconds Other interesting Feshpatents.com categories: Tyco , Unilever , Warner-lambert , 3m |
||
