| Expandable styrene resin particles, expandable beads, and foamed article -> Monitor Keywords |
|
|
  Expandable styrene resin particles, expandable beads, and foamed articleUSPTO Application #: 20070093563Title: Expandable styrene resin particles, expandable beads, and foamed article Abstract: A process of producing expandable styrene resin particles, wherein in suspension polymerization of styrene monomers, the concentration of oxygen in a reaction vessel is kept low at least in a late stage of the polymerization, and the resulting styrene resin particles are impregnated with an expanding agent before or after completion of the polymerization. Preferably, at a polymerization rate of 60% or higher, the concentration of oxygen in the reaction vessel is kept at 7 vol % or lower. When additional styrene monomers are added during the polymerization, they are added and adsorbed to styrene resin particles in the course of polymerization while the concentration of oxygen is kept low. By this method, the particles whose internal portion has a low molecular weight and surface portion has a high molecular weight are obtained. A foamed article produced from the particles has high strength and a good appearance. (end of abstract)
Agent: Antonelli, Terry, Stout & Kraus, LLP - Arlington, VA, US Inventors: Makoto Kunimi, Tetsuya Katou, Makoto Saitou, Hiroshi Nakaguki, Toshio Akima USPTO Applicaton #: 20070093563 - Class: 521056000 (USPTO) Related Patent Categories: Synthetic Resins Or Natural Rubbers -- Part Of The Class 520 Series, Synthetic Resins Or Natural Rubbers, Ion-exchange Polymer Or Process Of Preparing, Particle Which Is Expandible, Process Of Preparing An Expandible Particle, Or Process Of Expanding A Particle To Form A Cellular Product The Patent Description & Claims data below is from USPTO Patent Application 20070093563. Brief Patent Description - Full Patent Description - Patent Application Claims
CROSS-REFERENCE TO RELATED APPLICATION [0001] This application is a continuation application of U.S. application Ser. No. 10/901,970, filed Jul. 30, 2004, which is a continuation application of U.S. application Ser. No. 10/430,409, filed May 7, 2003, the contents of which are incorporated herein by reference. BACKGROUND OF THE INVENTION [0002] (i) Field of the Invention [0003] The present invention relates to expandable styrene resin particles and a production process thereof, expandable styrene beads, and a foamed article. [0004] (ii) Description of the Related Art [0005] An expandable styrene resin is used for a number of food containers, packing materials, cushioning materials and others by taking advantage of its excellent heat insulation properties, economy and sanitation. A foamed article thereof is produced by heating particles of the expandable styrene resin by steam or the like to be pre-foamed to a desired bulk density, subjecting the particles to an aging step, and filling the resulting particles into a mold to be foamed under heating again. The expandable styrene resin particles are required to have excellent expandability in the pre-expanding step or the expand-molding step in the mold under heating and to have high strength or an excellent appearance when molded into an article. [0006] Heretofore, to enhance the strength of the foamed article, some methods has been investigated, for example, increasing of the density of a molded article, or increasing of the thickness of the molded article itself. However, any of these methods can be hardly considered to be economical since the weight of the molded article increases and also have problems from an environmental standpoint. As for the expandable styrene resin particles, some methods has been investigated, for example, increasing the molecular weight, or controlling or reducing a kind or an amount of plasticizer for plasticizing the resin particles. [0007] On the other hand, to improve the expandability of the expandable styrene resin particles, a method of decreasing the molecular weight, a method of plasticizing the resin particles, a method of changing a composition ratio of expanding agents and other methods have been investigated. [0008] Such methods of enhancing the strength of the foamed article and such methods of improving the expandability are generally contradictory to each other, and hence, it has been difficult to simultaneously satisfy both the methods. [0009] For solving these problems, resin particles, whose outermost layer portion and central portion have a low molecular weight and middle portion has a high molecular weight, are proposed in Japanese Patent Laid-Open No. 295756/1996. [0010] However, the above particles have a problem that since the molecular weight of the outermost layer portion is low like the central portion, thermal fusion is promoted excessively at the time of heat-expand-molding, thereby degrading a surface finish of a molded article. [0011] Further, in Japanese Patent Laid-Open No. 188454/1995, resin particles whose surface layer portion has a higher molecular weight than that of the whole particle are disclosed. [0012] It is described in this publication that when the surface layer portion has an excessively high molecular weight, the expandability deteriorates and the appearance of the resulting molded article is degraded with a lower strength. This is assumed to be because the molecular weight of the central portion of the particles disclosed therein also becomes high as the molecular weight of the surface layer portion becomes high. That is, the above resin particles have a problem that the molecular weight of the surface layers cannot be sufficiently increased. [0013] Further, heretofore, to obtain the foamed articles having a good appearance, it was essential to eliminate gaps among beads completely when styrene beads filled in a mold are foamed under heating. However, it was difficult to eliminate all gaps among the beads. Under the circumstances, to eliminate as many voids as possible, the properties of expandable styrene resin particles themselves and molding techniques including the functions of molding machines and the like have been improved. [0014] For example, to improve the properties of the expandable styrene resin particles themselves, efforts were made to control the type and amount of plasticizer for plasticizing the resin particles, or to render the molecular weight lower. However, these methods lead to a reduction in the heat resistance of the resin particles and have a problem that the surface of a molded article is molten by heat-expanding at the time of molding, thereby increasing voids. [0015] Further, to improve molding techniques including the functions of molding machines and the like, the following have been studied. As for the molding machines, a control method in a heating step has been studied, and a method of using steam more efficiently was employed. As for molds, a method of using steam more effectively by, for instance, increasing the number of slits has been studied. However, these methods have problems that additional costs including costs for improving the machines and the molds are so large and it is difficult to improve all of these at once. SUMMARY OF THE INVENTION [0016] An object of the present invention is to provide expandable styrene resin particles capable of forming a molded article having high strength and having excellent expandability, expandable beads, and a foamed article. [0017] Further, another object of the present invention is to provide expandable styrene resin particles capable of forming a molded article having a good appearance and having excellent expandability, expandable beads, and a foamed article. [0018] A process for producing expandable styrene resin particles according to the present invention is characterized in that in suspension polymerization of styrene monomers, the polymerization reaction is allowed to proceed, keeping the concentration of oxygen in a reaction vessel low at least in the late stage of the polymerization. [0019] The process can prevent decreases in molecular weight of a surface portion. [0020] In the process of the present invention, the polymerization may be carried out with seeds. [0021] Further, the addition of styrene monomers in the late stage of polymerization leads to higher molecular weight of a surface portion, improving the strength of a molded article. The polymerization may be carried out without the addition of monomers. Continue reading... Full patent description for Expandable styrene resin particles, expandable beads, and foamed article Brief Patent Description - Full Patent Description - Patent Application Claims Click on the above for other options relating to this Expandable styrene resin particles, expandable beads, and foamed article patent application. ###  How KEYWORD MONITOR works... a FREE service from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like Expandable styrene resin particles, expandable beads, and foamed article or other areas of interest. ### Previous Patent Application: Polymeric composition, material produced and their applications Next Patent Application: Foam containing nanoparticles and process for producing a foam Industry Class: Synthetic resins or natural rubbers -- part of the class 520 series ### FreshPatents.com Support Thank you for viewing the Expandable styrene resin particles, expandable beads, and foamed article patent info. IP-related news and info Results in 0.76839 seconds Other interesting Feshpatents.com categories: Novartis , Pfizer , Philips , Polaroid , Procter & Gamble , |
||