| Electrophoretic method for the production of ceramic structures -> Monitor Keywords |
|
|
  Electrophoretic method for the production of ceramic structuresUSPTO Application #: 20070221500Title: Electrophoretic method for the production of ceramic structures Abstract: The invention relates to a method for producing ceramic structures and gradient structures whose particle size distribution has at least partly smaller values than the particle size distribution of the suspension from which the same are produced. According to the inventive method, a suspension containing ceramic particles is provided between a couple of electrodes, whereupon an electric field is applied to the couple of electrodes while the electrode surfaces of the couple of electrodes are placed perpendicular to a component of a gravitational field such that a fraction of the particles is deposited on the electrode of the couple of electrodes, which is located upstream of the component of the gravitational field, in the form of a ceramic structure. (end of abstract) Agent: Venable LLP - Washington, DC, US Inventors: Jurgen Hausselt, Melanie Dauscher, Holger Von Both USPTO Applicaton #: 20070221500 - Class: 204490000 (USPTO) Related Patent Categories: Chemistry: Electrical And Wave Energy, Non-distilling Bottoms Treatment, Electrophoresis Or Electro-osmosis Processes And Electrolyte Compositions Therefor When Not Provided For Elsewhere, Coating Or Forming Of Object, Using Bath Having Designated Chemical Composition (dcc), Resultant Coating Is Solely Inorganic The Patent Description & Claims data below is from USPTO Patent Application 20070221500. Brief Patent Description - Full Patent Description - Patent Application Claims
[0001] The invention relates to a method for producing ceramic structures (for example layers, filters, or micro-structures), as well as to structures and gradient structures produced with this method. [0002] Ceramic (micro-) structures, ceramic layers, and two-dimensional structures such as tiles, substrates, or filters are gaining in importance in many fields of technology. In particular, this is true for the so-called structural ceramics such as Al.sub.2O.sub.3, ZrO.sub.2,mullite, SiC, Si.sub.3N.sub.4, the functional ceramics such as BaTiO.sub.3 or PZT (lead-zirconate-titanate), and the so-called bio-ceramics, such as hydroxyl apatite Ca(OH) (PO.sub.4).sub.3, but also for mineral glass materials. Depending on the form, size and area of use for the parts or layers to be produced, the following production methods are used: dry pressing, powder-technological injection molding, hot molding, slip casting, foil casting, electrophoretic deposition from powder suspensions, and other methods which are followed by a sintering step. [0003] All known methods have in common that so-called feedstocks are used for the molding, wherein these feedstocks consist of ceramic powders and binders, dispersing agents, as well as slip additives for improving the workability. With the pressing methods, only small percentages by volume of these additives are added to the powders. With the injection molding, hot molding, slip molding, and foil casting methods, on the other hand, much higher percentages by volume of binders, dispersing agents, slip agents, polymers, waxes and suspension liquids such as water and alcohol are added. With these methods, the powder share ranges from 30 to 70 percentages by volume. For the electrophoretic deposition from watery or alcoholic suspensions, the percentage by volume of ceramic powder can range from approximately 5% to 50%. [0004] All methods furthermore have in common that the distribution of particles in the powder for the so-called green product is approximately the same as in the starting powder, the slip, the feedstock, or the suspension. In general, powders are used which have a relatively broad distribution in the form of so-called mono-modal powders, wherein these frequently follow normal distributions, logarithmic normal distributions, or so-called Rosin-Rammler distributions. In part, powders are also used which are present in the form of complex multi-modal distributions. [0005] The roughness of the produced parts and layers, as well as their pore sizes and to some degree also their structure following the sintering, are influenced by the distribution of particle sizes. For example, the rough components of the powder that is used determine the surface roughness. The distribution of pore sizes in the filter membranes is correlated to the particle size: the larger the powder particles, the larger the pores that develop. For that reason, only particles below a specific size, e.g. 500 nm, can therefore be used with traditional production methods to achieve, for example, especially smooth layers or micro-structures or to obtain extremely small pore sizes. For this, the powders must first be fractionated and graded in a complicated manner before the starting feedstock is produced, for example by means of screening or wind-sifting, and only the desired powder fraction should be introduced into the feedstock. [0006] For cost reasons, these additional and very involved processing steps are out of the question for most applications. Particularly smooth layers with peak-to-valley heights below 1 .mu.m and micro-structures with surface details in the .mu.m range can therefore not be produced by using traditional, commercially available powders with powder sizes that are generally in the range above 1 .mu.m. [0007] Starting from this point, it is the object of the present invention to provide methods for producing ceramic structures which are not subject to the aforementioned disadvantages and restrictions. [0008] This object is solved with the method as defined in claim 1. The dependent claims describe advantageous embodiments of the invention. [0009] The method according to the invention is based on combining the electrophoretic deposition and the sedimentation due to gravitational forces and/or centrifugal forces. The electrophoretic deposition of ceramic particles from particle suspensions as a method for producing ceramic layers is known (Heavens, S.N.: Electrophoretic Deposition as a Processing Route for Ceramics; in Binner, J. (Ed.), Advanced Ceramic Processing and Technology, Vol. 1, Noyes Publ., Park Ridge, N.J. U.S.). Attempts have recently been made to use this technique also for realizing ceramic micro-structures (Both, H. von; Hausselt, J.: 1.sup.st Intern. Conf. on Electrophoretic Deposition, Banff, Canada, 2002). For this, an electric field is applied between two electrodes submerged in the powder suspension, causing a flow of charged particles to move toward one of the two electrodes and causing the particles to be deposited thereon. [0010] The principles of electrophoresis have long been known. Corresponding theoretical descriptions disclose that in the size range for ceramic powders used for technical applications, meaning in the range between 10 nm and 100 .mu.m, the electrophoretic mobility of the powder particles for the most part does not depend on their size (Nitzsche, R.; Simon, F.: "TECHNISCHES MESSEN" [Technical Measuring] Volume 64, pages 106-113, 1997). All particle sizes occurring in the suspension should therefore be deposited with substantially the same speed on the electrically conductive substrate. The deposited layers consequently should have the same distribution of particle sizes as the suspension, albeit packed with substantially higher density. [0011] Our own measurements confirm that the migration rate V.sub.E in the electric field E depends not only on the suspension medium (e.g. watery or alcoholic), the chemical composition of the powder (e.g. Al.sub.2O.sub.3, ZrO.sub.2, SiO.sub.2), and the added dispersing and binding agents, but can also depend to a small degree on the existing particle size. Depending on the system, it is possible to observe different, but always small, dependencies of the migration rate on the particle size. [0012] Experiments with alcoholic Al.sub.2O.sub.3 suspensions have shown that smaller particles are deposited slightly faster than larger ones, but that this effect is not sufficient for a technical use, for example for the electrophoretic in-situ-fractionizing. For the electrophoretic deposition, the mobility .mu. and the migration rate v.sub.E consequently depend on the particle size (radius r) in the electric field E, wherein: dv.sub.E/dr.ltoreq.0 (1a) and, owing to v.sub.E =.mu.E d.mu./dr.ltoreq.0 (1b) applies. [0013] In watery suspensions with spherical SiO.sub.2 particles having diameters between 200 nm and 1200 nm, on the other hand, larger particles will be deposited slightly faster than finer particles. Thus, for the electrophoretic deposition, the mobility .mu. and the migrating rate v.sub.E depend on the particle size (radius r) in the electrical field E, wherein: dv.sub.E/dr.gtoreq.0 (1c) and, owing to of v.sub.E =.mu.E d.mu./dr.gtoreq.0 (1d) applies. [0014] For a number of applications, it is desirable to have a deposition of only specific fractions, such as the share of fine particles in a predetermined distribution of particle sizes. For the above-described reasons this cannot be achieved with the electrophoretic deposition according to the prior art. The known technique of electrophoretic deposition from powder suspension furthermore cannot be used for applications using a single deposition and without changing the powder suspension, for which initially only rough particles are deposited and, with progressing time and layer thickness, smaller powder particles are deposited gradually or continuously. [0015] According to the invention, a field which causes a particle speed that depends on the particle size is superimposed on the electrical field which causes a particle speed that is mostly independent of the particle size in the direction of the electrical field. For this type of application, the deposit by sedimentation which depends on the particle size is suitable, either in a constant, locality-independent gravitation field (gravity sedimentation) or in a variable and locality-dependent gravitation field (centrifuging). [0016] This is in contrast to the standard electrophoresis where the effective gravitational force resulting from the earth's gravitational field, which is undesirable for specific applications, is eliminated with the aid of suitable measures such as a special arrangement of the electrodes and especially by stirring the suspension. [0017] For individual spherical particles with a radius r and a density p, which are dispersed (suspended) in a liquid with the density p.sub.F and the viscosity .eta., this results in a sedimentation rate v based on the Stokes law, under the effect of an acceleration b: 6.pi..eta.rv=(4.pi./3)r.sup.3(p-p.sub.F)b (2) [0018] The sedimentation rate v is therefore proportional to r.sup.2 if the viscosity .eta. is constant. Even in cases of deviations from the equation 2 because of particle shapes which generally differ from the spherical form and at higher concentrations for the suspensions, the qualitative relation remains in place, which indicates that the sedimentation rate increases with increasing particle size and increasing difference in the density values. In any case, the following applies: dv/dr >0. (3) [0019] If the direction of the migration rate in the electric field is counter to the sedimentation rate in the gravitational field, a critical particle size r.sub.c is obtained for each electrical field intensity E and for each acceleration b in the gravitational field, wherein the effects of both fields cancel each other out and the particle is suspended. All particles with r>r.sub.c move in the direction of the gravitational field while all particles with r <r.sub.c move in the direction of the electrical field. Depending on the selection of the electrical field intensity E and the acceleration b (e.g. by varying the speed in a centrifuge), freely selectable fractions of the original distribution of particle sizes can for the most part be deposited on an electrically conductive substrate. [0020] In general, the angle between the directions of the electrical field and the gravitational field is selected such that a speed component which depends on the particle size can be added or subtracted for a mostly particle-size independent speed distribution in the electric field. The effect of the constant and locality- independent acceleration due to gravity by itself makes it possible to ensure that the share of fine particles in a distribution is advantageously deposited on an electrode by varying the electrical field intensity and the angle between both field directions. The electrical and the gravitational fields are preferably arranged parallel to each other, meaning the electrodes are positioned substantially perpendicular to the direction of the gravitational field (e.g. horizontally in the gravity field). [0021] In contrast to the traditional electrophoresis, our invention provides that one fraction of the suspended particles is deposited under the effect of gravity on the upper electrode. The fraction deposited in the form of a ceramic structure generally is distinguished in that its distribution of particle sizes differs from the distribution of particle sizes in the suspension, which is not the case with the standard electrophoresis. Since the finer particles are preferably deposited, the distribution of particle sizes in the ceramic structure has lower values than the distribution of particle sizes in the suspension. [0022] According to one preferred embodiment of the invention, the distribution of the particle sizes to be deposited can be influenced by freely selecting not only the absolute value, but also the point in time for superimposing the sedimentation by gravity on the electrical field. The respectively desired limit for the deposited size fraction can be adjusted by varying the electrical field intensity. [0023] A particularly preferred embodiment of the invention is obtained by superimposing a gravitational field with variable absolute value on an electrical field with variable absolute value, as shown in particular with the centrifuging operation where centrifugal forces occur. While activated, the generated gravitational field is directed toward the outside, relative to the axis of rotation of the centrifuge. As a result of this arrangement, the share of micro particles in the suspension is deposited according to the invention in the form of a ceramic layer on the inner electrode. [0024] The distribution of particle sizes to be deposited can furthermore be influenced by not only selecting the absolute values of the electrical field and the gravitational field of the centrifugal acceleration over broad ranges, but also by freely selecting the points in time when both fields are activated and/or shut down. Continue reading... Full patent description for Electrophoretic method for the production of ceramic structures Brief Patent Description - Full Patent Description - Patent Application Claims Click on the above for other options relating to this Electrophoretic method for the production of ceramic structures patent application. ###  How KEYWORD MONITOR works... a FREE service from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like Electrophoretic method for the production of ceramic structures or other areas of interest. ### Previous Patent Application: Quickly activatable structure of gas sensor element Next Patent Application: Method and device for collecting suspended particles Industry Class: Chemistry: electrical and wave energy ### FreshPatents.com Support Thank you for viewing the Electrophoretic method for the production of ceramic structures patent info. IP-related news and info Results in 1.31636 seconds Other interesting Feshpatents.com categories: Canon USA , Celera Genomics , Cephalon, Inc. , Cingular Wireless , Clorox , Colgate-Palmolive , Corning , Cymer , |
||
