Microporous carbon and method for making the same   

TECHNICAL FIELD

The present disclosure relates generally to microporous carbon and a method for making the same.

The use of hydrogen as an alternative to conventional fuels, especially for automotive applications, is currently being investigated. As such, the development of suitable hydrogen storage media for commercial hydrogen powered vehicles is also of interest. Current techniques for transporting and storing hydrogen include liquid hydrogen, compressed hydrogen, chemisorption and physisorption. Porous carbon materials (e.g., activated carbons, mesoporous carbons, porous carbon fibers and carbide-derived carbons) are widely used as adsorbents in industrial applications because of the high surface area, low cost and relatively good stability.

SUMMARY

A carbon material includes a carbonized composite formed from a substantially homogeneous composite including a carbon precursor and an activation agent that is soluble in a solution including the carbon precursor. Micropores having a substantially uniform size distribution are formed throughout the carbonized composite. At least 90% of a total pore volume of the carbon material is composed of micropores, and 10% or less of the total pore volume is composed of mesopores and macropores. A surface area of the carbon material ranges from about 1400 m2/g and 3000 m2/g. A method for forming the carbon material is also disclosed herein.

BRIEF DESCRIPTION OF THE DRAWINGS

Features and advantages of examples of the present disclosure will become apparent by reference to the following detailed description and drawings.

FIG. 1 is flow diagram illustrating an example of the synthesis of the microporous carbon material;

FIG. 2 is a graph depicting nitrogen adsorption isotherms of microporous carbons prepared with different ratios of activation agent and carbon precursor;

FIG. 3 is a graph illustrating the effect of potassium hydroxide (KOH) content on the surface area of microporous carbons;

FIG. 4 is a graph illustrating the effect of carbonization/activation temperature on the surface area of microporous carbons;

FIG. 5 is a graph illustrating the effect of carbonization/activation time on the surface area of microporous carbons;

FIG. 6 is a graph depicting excess hydrogen absorption isotherms of microporous carbons at 77K and room temperature;

FIG. 7 is a graph illustrating the effect of KOH content on hydrogen uptake at 77K of the microporous carbons;

FIG. 8 is a graph illustrating the effect of carbonization/activation time on the hydrogen uptake at 77K of the microporous carbons;

FIG. 9 is a graph illustrating the effect of carbonization/activation temperature on the hydrogen uptake at 77K of the microporous carbons; and

FIG. 10 is a graph depicting the relationship of surface area and hydrogen absorption capacity at 77K and 40 bar.

DETAILED DESCRIPTION

Embodiments of the method disclosed herein advantageously enable control over the porosity of microporous carbon materials. It is believed that homogeneous mixing of the carbon precursor and activation agent contributes to relatively uniform pore size distribution and high surface area of the formed porous carbon materials. As used herein, the phrase “relatively uniform pore size distribution” means that 90% or more of the pores in the material have a diameter equal to or less than 2 nm, and as such, the material does not have a broad distribution of pore sizes. In other words, 90% or more of the total pore volume is made up of micropores (≦2nm), and 10% or less of the total pore volume is made up of mesopores (2 nm-50 nm) and macropores (greater than 50 nm).

The microporous carbon materials disclosed herein may advantageously be used in a variety of applications, including catalysis, gas purification, fuel cell and battery electrodes, and gas storage. More particularly, the microporous carbon materials may be used, for example, as hydrogen storage media, catalyst supports, adsorbents, or electrodes.

Referring now to FIG. 1, a non-limiting example of the method for making the microporous carbon material is depicted. Very generally, the method includes preparing a carbon precursor solution; mixing an activation agent in the carbon precursor solution to form a substantially homogeneous mixture; polymerizing the substantially homogeneous mixture to form a substantially homogeneous composite; and carbonizing the substantially homogeneous composite to form the microporous carbon material.

Suitable carbon precursors include phenolic resin oligomers, resorcinol, or phloroglucinol based resin oligomers. It is to be understood that such materials are used as a source or precursor of carbon that makes up the final material. The carbon precursor solution may be formed by reacting two or more starting materials (which form the carbon precursor) in a liquid medium in the presence of a catalyst. The starting materials will depend, at least in part, on the desirable carbon precursor that is to be formed. As shown in FIG. 1, a phenolic resin oligomer solution is prepared by reacting phenol and formaldehyde (in the presence of KOH or some other suitable catalyst) in a liquid medium (e.g., water or a mixture of water and alcohol, such as ethanol).

It is believed that the carbon precursor solutions disclosed herein are better starting materials than fully polymerized materials, at least in part because the activation agent can readily dissolve into the carbon precursor solution to form a homogeneous solution.

Once the carbon precursor solution is prepared, the activation agent is added thereto. The carbon precursor/activation agent mixture is stirred to achieve substantially uniform dispersal of the carbon precursor molecules and activation agent molecules in the solution. Such a homogeneous solution results, at least in part because the activation agent is soluble in the carbon precursor solution. It is believed that the homogeneity of the solution contributes to the substantially uniform pore size distribution and high surface area of the resulting microporous carbon material. Furthermore, the activation agent may also act as a catalyst for the synthesis and subsequent polymerization of the carbon precursor.

In one non-limiting example, potassium hydroxide (KOH) is used as the activation agent to form generally uniformly sized micropores in the carbon material. Other non-limiting examples of suitable activation agents include sodium hydroxide (NaOH), potassium carbonate, or sodium carbonate.

It is to be understood that the amount of activation agent used is sufficient to form a material having at least 90% of its total pore volume composed of micropores, and 10% or less of its total pore volume composed of mesopores and macropores. In such materials, the macropore volume is at or near 0%. As a non-limiting example, the weight ratio of activation agent to carbon precursor ranges from about 1 to about 3.

Furthermore, the surface area of the microporous carbon material may be adjusted by controlling the amount of the activation agent mixed into the carbon precursor solution. A desirable amount generally results in the surface area ranging from about 1400 m2/g or 2000 m2/g to about 3000 m2/g (as determined, for example, from Brunauer, Emmett and Teller (BET) nitrogen sorption surface area measurements).

The substantially homogeneous carbon precursor/activation agent solution is then exposed to heating at a predetermined temperature for a predetermined time. In a non-limiting example, heating is accomplished at about 160° C. for about 12-24 hours. Heating evaporates any solvent (e.g., water, or water and alcohol) and initiates cross-linking and polymerization, thereby forming a homogenous polymer/activation agent solid composite. A homogeneous phenolic resin oligomer/KOH solid composite is shown in FIG. 1.

The solid composite is then carbonized and activated at the same time by heating to a temperature ranging from about 500° C. to about 900° C. under an inert atmosphere (e.g., nitrogen or argon) for a time ranging from about 0.5 hours to about 8 hours. As indicated, the heating step causes the polymer to be converted to carbon while the activation agent acts as a chemical activation reagent on the carbon to create porosity. As such, the heating process results in the formation of the final microporous carbon material.

The final product may then be washed with dilute hydrogen chloride one or more times and with hot water several times to remove any residual activation agent and other impurities.

To further illustrate embodiment(s) of the present disclosure, an example is given herein. It is to be understood that this example is provided for illustrative purposes and is not to be construed as limiting the scope of the disclosed embodiment(s).

Sample Preparation

Oligomeric phenol-formaldehyde was synthesized by reacting 13 mmol phenol, 26 mmol formaldehyde and 1.3 mmol potassium hydroxide at 70° C. for about 1 hour. A desired amount of potassium hydroxide solution (5M) was added gradually into the phenol-formaldehyde oligomer solution under stirring. Various samples (C-1 through C-18 in Table 1 below) were made using different ratios of KOH to oligomeric phenol-formaldehyde. The oligomer-KOH solutions were heated in an oven at 160° C. overnight. During this heating process, the phenol-formaldehyde oligomers continued to crosslink and polymerize to form a thermoset, carbonizable polymer under the catalysis of potassium hydroxide.

311 The polymers were then carbonized/activated at high temperature (ranging from about 500° C. to about 900° C.) under an inert atmosphere. The final carbon materials were rinsed several times with dilute hydrochloric acid and de-ionized water, and dried in an oven at 150° C. overnight.

Sample Characterization

The samples were characterized using nitrogen sorption surface area measurements (Micromeritics ASAP 2010 operated at 77K). Cryogenic hydrogen sorption measurements at high pressures were performed using a PCTPro 2000 (Hy-Energy Scientific Instruments) at 77K and room temperature.

Results

High surface area microporous carbon materials were obtained using the process disclosed herein. FIG. 2 illustrates nitrogen adsorption isotherms of microporous carbons (samples C-1 and C-4) prepared with different ratios of activation agent and carbon precursor. Table 1 shows the detailed synthesis conditions and the hydrogen absorption capacities of the obtained porous carbons at 77K and 40 bar.

TABLE 1 BET surface areas and hydrogen absorption capacities (at 77K and 40 Bar) of the porous carbon materials Weight ratio Carbonization/ Carbonization/ Excess Hydrogen Sample of KOH to Activation Activation BET surface Absorption number oligomer Temp. (° C.) Time (hour) area (m2/g) (wt. %) C-1 1 700 4 1424 2.81 C-2 1.5 700 4 1662 3.69 C-3 2 700 4 2711 5.25 C-4 2.2 700 4 2811 5.68 C-5 2.25 700 4 2943 5.75 C-6 2.5 700 4 2466 4.86 C-7 1 800 4 1587 3.30 C-8 1.5 800 4 2075 3.91 C-9 2 800 4 2698 5.02 C-10 2.25 800 4 2441 4.84 C-11 2.5 800 4 1992 3.33 C-12 2 700 0.5 1627 3.05 C-13 2 700 1 1752 3.32 C-14 2 700 2 2438 4.30 C-15 2 700 8 2625 4.51 C-16 2 500 4 1627 3.50 C-17 2 600 4 2228 4.36

Download full PDF for full patent description/claims.




You can also Monitor Keywords and Search for tracking patents relating to this Microporous carbon and method for making the same patent application.
###